PENGARUH JUMLAH LAPISAN WIRE MESH TERHADAP KEKUATAN MEKANIK PADA MATERIAL FERRO-GEOPOLYMER BERSERAT

Viandika, Yusma (2015) PENGARUH JUMLAH LAPISAN WIRE MESH TERHADAP KEKUATAN MEKANIK PADA MATERIAL FERRO-GEOPOLYMER BERSERAT. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Geopolimer merupakan material polimer anorganik aluminosilikat dengan rantai Si-O-Al yang disintesis dari material pozzolan yang kaya akan silika dan alumina dengan larutan pengaktif natrium hidroksida dan bahan pengikat Na-Silikat. Geopolimer dianggap memiliki sifat kimia dan fisika yang baik sebagai pengganti semen portland. Dengan penambahan serat dan kawat kasa pada material geopolimer yang berfungsi sebagai pengisi dan penguat akan menghasilkan sifat mekanik material ferro-geopolymer berserat menjadi lebih baik. Analisis pengaruh jumlah lapisan kawat kasa terhadap kekuatan mekanik material ferro-geopolymer berserat dilakukan untuk mengetahui jumlah lapisan kawat kasa yang optimal untuk aplikasi panel pemisah ruangan. Dengan komposisi serat kenaf 1% volume, variasi jumlah lapisan kawat kasa 1 lapis, 2 lapis dan 3 layer lapis serta tanpa kawat kasa sebagai hasil pembanding. Analisis menggunakan software berbasis metode elemen hingga diharapkan mampu mengetahui kekuatan struktur dan deformasi dari papan ferro-geopolymer berserat dengan hasil yang mendekati aktual. Hasil dari penelitian ini dengan penambahan 1 lapis kawat kasa meningkatkan nilai kuat tarik sebesar 53,1%, penambahan 2 lapis kawat kasa meningkatkan kuat tarik 63,5% serta penambahan 3 lapis kawat kasa meningkatkan nilai kuat tekan 79,3%. Perbandingan nilai deformasi dari hasil analisis menggunakan software MSC. NASTRAN dengan nilai deformasi hasil uji fleksural diperoleh nilai deformasi pada material ferro-geopolymer berserat kenaf sebesar 0,345 mm dan 0,327 mm. Dan untuk nilai standar deformasi maksimal papan gipsum konvensional adalah sebesar 0,545 mm. Maka dari itu, papan ferro-geopolymer dengan penambahan serat kenaf layak untuk dijadikan panel pemisah ruangan. Kata kunci : Geopolimer, Ferro-Geopolymer, Wire Mesh ABSTRACT Geopolymer is a polymer anorganic aluminosilicat material with chain Si-O-Al synthesized from pozzolan material that rich of silica and alumina with liquid activator sodium hidroxide and sodium silicat as fastener. Geopolymer considered having good chemistry and physics properties as a substitute for cement portland. By the addition of fiber and wire mesh in geopolymer material that serves as a filler and strengthener will produce better mechanical properties of fibrous ferro-geopolymer material. Analysis effect of wire mesh layer quantity to mechanical strength of fibrous ferro-geopolymer conducted to determine wire mesh layer quantity that optimal for the application as room separator panel. With the composition of kenaf fiber volume 1%, variations of wire mesh layer quantity 1 layer, 2 layers and 3 layers, and also without wire mesh as comparator result. Analysis using software based finite element method that expected be able to know the structure strength and deformation of fibrous ferro-geopolymer board with the result that closer to actual test. The result of this research is with addition of 1 layer wire mesh increase the value of tensile strength 53,1%, addition of 2 layers wire mesh increase tensile strength 63,5% and addition of 3 layers wire mesh increase the tensile strength 79,3%. Deformation value comparison from the analysis result using software MSC. NASTRAN and deformation value from flexural test of kenaf fibrous ferro-geopolymer material is 0,345 mm and 0,327 mm. And for maximum standard value of conventional gypsum board is 0,545 mm. Therefore, ferro-geopolymer board by the addition of fiber kenaf is worthy to be room separator panel. Keywords: Geopolymer, Ferro-Geopolymer, Wire Mesh

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Desain dan Manufaktur > Teknik Desain dan Manufaktur
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 04 Sep 2018 05:30
Last Modified: 04 Sep 2018 05:30
URI: http://repository.ppns.ac.id/id/eprint/323

Actions (login required)

View Item View Item