STUDI PENGARUH SUHU BENDA UJI MATERIAL ALUMINIUM 5083 PADA PENGUJIAN PENETRAN

Asyari, Choirul (2015) STUDI PENGARUH SUHU BENDA UJI MATERIAL ALUMINIUM 5083 PADA PENGUJIAN PENETRAN. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Penetran tes merupakan salah satu jenis NDT (Non Destructive Test) yang relatif mudah dan cepat pelaksanaannya serta murah biayanya dibandingkan dengan uji NDT yang lain. Pengujian ini adalah cara yang paling peka untuk menentukan adanya cacat halus pada permukaan seperti retak, lubang halus atau kebocoran. Pada dasarnya pengujian ini menggunakan prinsip kapilaritas sebagai cara kerjanya. Pengujian ini dilakukan pada material aluminium 5083 dengan sambungan las MIG dimana perlakuan pengujian tetap sama seperti prosedur pengujian penetran tes dengan penetrating time 10 menit dan developer time 10 menit, hanya saja proses pengujian dilakukan dengan 3 macam suhu yang berbeda-beda. Pertama pengujian suhu benda uji 0˚C-5˚C, yang kedua pengujian suhu benda uji 10˚C-15˚C dan yang ketiga pengujian suhu benda uji 20˚C-25˚C. Berdasarkan pengujian yang telah dilakukan diketahui bahwa suhu mempunyai pengaruh terhadap pengujian penetran. pada suhu benda uji 0˚C-5˚C tidak ada indikasi cacat yang terbentuk. Tetapi pada pengujian suhu benda uji 10˚C-15˚C ditemukan empat indikasi cacat yang terbentuk, yang pertama indikasi cacat rounded dengan ukuran 5x4 mm, yang kedua juga indikasi cacat rounded dengan ukuran 3x3 mm, yang ketiga indikasi cacat rounded dengan ukuran 3x2 mm. Dan yang ke empat juga indikasi cacat rounded dengan ukuran 5x3. Sedangkan pada pengujian suhu benda uji 20˚C-25˚C ditemukan tujuh indikasi cacat dan itu semua jenis indikasinya cacat rounded, yang pertama indikasi cacat rounded dengan ukuran 5x5 mm, yang kedua indikasi dengan ukuran 4x4 mm, yang ketiga indikasi cacat rounded dengan ukuran 5x3 mm, yang keempat indikasi cacat dengan ukuran 6x3 mm, yang ke lima indikasi cacat dengan ukuran 3x2 mm, yang ke enam indikasi cacat dengan ukuran 3x3 mm, dan yang telakhir indikasi cacat dengan ukuran 3x2 mm. Di situ tidak terdapat jenis indikasi cacat linier yang terbentuk. . Kata kunci : uji tanpa merusak, uji penetran, suhu, benda uji. ABSTRACT Penetrant test is one type of NDT (Non Destructive Test) is relatively easy and fast implementation and low cost compared to other NDT test. This test is the most sensitive way to determine the presence of smooth surfaces like cracks, a fine or leaks smooth. Basically, this test using the principle of capillarity a show it works. The test is performed on aluminium 5083 steel with welded joints MIG where treatmen tremains the same test as the test penetrant testing procedure with penetrating time10 minutes and developer time 10 minutes, it's just that the testing processis done with three kinds of different temperatures. The first test specimen temperature of 0˚C-5˚C, the second test specimen temperature of 10˚C-15˚C and the third test specimen temperature 20˚C-25˚C. Based on the testing that has been made known that temperature has an influence on penetrant testing. The specimen temperature 0˚C-5˚C there is no indication that defect sare formed. But the test specimen temperature 10˚C-15˚C found four indications of defects, the first indication of a rounded defect with size 5x4 mm, the latter is also an indication of rounded defects with size 3x3 mm , a the third indication rounded defects with size 3x2 mm. And the four also an indication of the defects rounded to the size of the 5x3 mm. While at the test temperature 20˚C-25˚C of specimen found seven defect indication and that’s all kind of indication of her crippled rounded, the first indication of a rounded defect with size 5x5 mm, the latter is also an indication of rounded defects with size 4x4 mm, which is the third indication rounded defects with size 5x3 mm, the four the indication rounded defect again to the size of 6x3 mm, the five indication rounded defects with size 3x2 mm, the six indication rounded defects with size 3x3 mm, and the seven indication rounded defect again to the size of 3x2 mm. in it there is no kind of indication of a linier. Keywords: Non destructive test, penetranttest, temperature, weld metal.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Bangunan Kapal
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 30 Aug 2018 06:29
Last Modified: 30 Aug 2018 06:29
URI: http://repository.ppns.ac.id/id/eprint/303

Actions (login required)

View Item View Item