Sholatun, Moch Arnold Hazirni (2015) STUDI PENGARUH KUAT ARUS TERHADAP DEFORMASI PADA SAMBUNGAN LAS PIPA ALUMINIUM ASTM SCHEDULE 80 DENGAN PENGELASAN GTAW. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.
Full text not available from this repository.Abstract
ABSTRAK Pipa aluminium ASTM schedule 80 merupakan produk yang banyak diaplikasikan dalam dunia maritim sebagai bahan yang baik dalam menahan tekanan aliran dari dalam, mengatasi kegetasan pipa dan ketahanannya terhadap korosi air laut. Dalam penerapan dikapal banyak digunakan pada saluran bilga dan juga saluran-saluran yang menghantarkan suatu zat yang bersifat kimia dan juga saluran gas lainya. Penelitian ini menggunakan material Pipa aluminium ASTMschedule 80 yang menggunakan pengelasaan GTAW dengan posisi las mendatar(1G) dan ketebalan pipa 2 mm, diameter pipa 1.5inci, elektroda yang digunakan adalah ER5356 dengan diameter 2,4 mm dan kuat arus pengelasan antara 110-119 Ampere yang berpatokan pada Standar Kerja Lapangan Milik PT.Orela Shipyard. Untuk perubahan struktur pipa pasca pengelasan digunakan metode pelurusaan, dan untuk mengetahui adanya cacat las yang terjadi dalam permukaan material digunakan penetrant test. Dari pengujianyang telah dilakukan didapatkan bahwa pengelasan Pipa aluminium ASTMschedule 80 dalam metode kelurusaandari ketiga specimen yang mempunyai nilai deformasi tertinggi adalah pada specimen 3 sedangkan nilai deformasi yang terendah pada specimen 1. Dalam penetrant test specimen 2 merupakan spesimen dengan cacat terbanyak. Dari ketiga spesimen yang diuji terdapat cacat, cacat tersebut masih memenuhi standart uji kriteria. Kata kunci: Pipa aluminium ASTMschedule 80, Ampere, GTAW, Metode pelurusaan, Pengujian Penetrant test. ABSTRACT An aluminium pipe ASTM schedule 80 is a product of many maritime application in the world material as a good resistance to brittleness and seawater corrosion. Its applications are widely used in onboard bilga channels and also channels that deliver a substance that is chemically and others. In this research material are used an aluminium pipe ASTM schedule 80 welded GTAW pipe horizontal pipe with (1G) with a thickness of 2 mm pipe, 1,5 inch diameter pipe, the electroda is ER5356 with 2,4 mmdiameter, and with a strong flow of welding between 100 to 119 Ampere is based on Field Work Standards Property PT.Orela Shipyard. To change the structure of the pipe before and after the welding straightness test used, and to know the existence of welding defects that occur in use penetrant test. From the test that was done it was found that welding with an aluminium pipe ASTM schedule 80 in straightness test the highest value is specimen deformation 3, while the lowest is a specimen deformation 1. In the penetrant test the specimen 2 has the most defect. From the three speciment has test, the defect can be accept. Keywords: An aluminium pipe ASTM schedule 80, Ampere, GTAW, Straightness test, Penetrant test.
| Item Type: | Thesis (Diploma) |
|---|---|
| Subjects: | T Technology > T Technology (General) |
| Divisions: | Jurusan Teknik Bangunan Kapal > D3 Teknik Bangunan Kapal |
| Depositing User: | Unnamed user with email repository@ppns.ac.id |
| Date Deposited: | 30 Aug 2018 05:36 |
| Last Modified: | 30 Aug 2018 05:36 |
| URI: | http://repository.ppns.ac.id/id/eprint/292 |
Actions (login required)
 |
View Item |