ANALISA PERLAKUAN PREHEAT TERHADAP KETAHANAN STRESS CORROSION CRACKING DAN TRANSFORMASI MIKROSTRUKTUR PADA DAERAH HEAT-AFFECTED-ZONE PENGELASAN P265GH STEEL DALAM PROYEK ASSEMBLY COOLING TOWER

PRATAMA, KEVIN SETIA RISKY (2017) ANALISA PERLAKUAN PREHEAT TERHADAP KETAHANAN STRESS CORROSION CRACKING DAN TRANSFORMASI MIKROSTRUKTUR PADA DAERAH HEAT-AFFECTED-ZONE PENGELASAN P265GH STEEL DALAM PROYEK ASSEMBLY COOLING TOWER. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Variasi preheat menimbulkan perbedaan koefisien pemuaian dan penyusutan pada material yang dilas dan menyebabkan terjadi regangan yang dapat menyebabkan distorsi dan tegangan sisa dimana tegangan ini akan mempengaruhi terjadinya stress corrosion cracking dan transformasi mikrostruktur pada daerah HAZ. Pada penelitian ini akan dianalisis ketahanan stress corrosion cracking dan transformasi mikrostruktur pada daerah HAZ dengan variasi preheat pada material mild steel P265GH. Metode pengujian yang akan dilakukan untuk menganalisis terjadinya stress corrosion cracking adalah dengan menggunakan spesimen U-bend yang mengacu pada standard ASTM G 30 serta pengujian stress corrosion cracking pada lingkungan magnesium nitrat mendidih. Pengujian penetrant dilakukan untuk mengobservasi retak yang terjadi. Dari hasil penelitian, didapatkan preheat menyebabkan tegangan thermal yang terjadi pada masing-masing variasi berbeda-beda. Perbedaan tegangan yang terjadi pada hasil pengelasan material mild steel P265GH di beberapa variasi preheat, berpengaruh terhadap ketahanan stress corrosion cracking pada pengujian di lingkungan Mg(NO3)2 mendidih selama 48 jam dan transformasi pada daerah HAZ mengalami penambahan butir menjadi ferrite acicular dan widmanstatten ferrite. Kata kunci : preheat, stress corrosion cracking, transformasi mikrostruktur, heat-affected-zone. ABSTRACT Preheat variations cause different coefficients of expansion and shrinkage on welded material and cause strain that can cause distortion and residual stress where this stress will affect the occurrence of stress corrosion cracking and microstructural transformation in HAZ area. In this research we will analyze the stress corrosion cracking and microstructure transformation in HAZ area with preheat variation on mild steel P265GH material. Test methods to be performed to analyze the occurrence of stress corrosion cracking is using U-bend spesimen s that refer to ASTM G 30 standard and stress corrosion cracking test on boiling magnesium nitrate environment. Penetrant testing is performed to observe the cracks that occur. From the results of the research, the preheat caused the thermal voltage that occurs in each preheat variations is different. The differences in stresses on mild steel P265GH welding results in some variations of preheat, have an effect on the stress corrosion cracking resistance in the Mg(NO3)2 boiling for 48 hours and the transformation in the HAZ area grew into ferrite acicular and widmanstatten ferrite. Keywords: preheat, stress corrosion cracking,, microstructural transformation, heat-affected-zone.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 06:05
Last Modified: 05 Oct 2018 06:05
URI: http://repository.ppns.ac.id/id/eprint/1340

Actions (login required)

View Item View Item