ANALISIS PENGARUH TEMPERATUR, KADAR GARAM DAN KECEPATAN AIR LAUT TERHADAP KETAHANAN KOROSI BUTT JOINT MIG WELD DI KONSTRUKSI LAMBUNG CREW BOAT ALUMINIUM 5083

Zuriah, Dara Lathiful (2017) ANALISIS PENGARUH TEMPERATUR, KADAR GARAM DAN KECEPATAN AIR LAUT TERHADAP KETAHANAN KOROSI BUTT JOINT MIG WELD DI KONSTRUKSI LAMBUNG CREW BOAT ALUMINIUM 5083. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Indonesia merupakan negara kepulauan yang panjang garis pantai yang mencapai 95.181 km. Indonesia mengalami perkembangan yang sangat pesat, terutama dalam dunia maritim. Dalam pembuatan kapal dibutuhkan material dan penyambungan yang baik dan bermutu terutama lambung kapal. Salah satu jenis aluminium yang digunakan konstruksi kapal adalah aluminium tipe 5083. Proses pengelasan GMAW lebih efisien untuk logam aluminium. Material kapal lebih sering tercelup pada lingkungan basah (air laut). Lingkungan air laut sangatlah korosif, sehingga tidak menutup kemungkinan terjadi korosi dan disetiap daerah lingkungan laut memiliki laju korosi yang berbeda-beda. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh kadar garam, temperatur, kecepatan air laut dan hubungan ketiga variabel tersebut terhadap ketahanan korosi logam las aluminium 5083 butt joint MIG weld. Adapun metode pengujian yang digunakan adalah dengan menggunakan pengujian polarisasi linier dengan larutan NaCl. Berdasarkan grafik tafel hasil pengujian polarisasi linier, temperatur, konsentrasi garam dan kecepatan aliran lingkungan mempengaruhi laju korosi. Semakin tinggi temperatur maka semakin tinggi laju korosi nya, hal ini terbukti dengan nilai laju korosi yang paling besar diperoleh suhu tertinggi yaitu 40 0 C dengan nilai 0.19984 mmy. Sedangkan semakin tinggi kadar garam maka semakin tinggi laju korosi nya, hal ini terbukti dengan nilai laju korosi yang paling besar diperoleh kadar garam tertinggi yaitu 15% dengan nilai 0.23852 mmy. Dan semakin tinggi kecepatan maka semakin tinggi laju korosi nya, hal ini terbukti dengan nilai laju korosi yang paling besar diperoleh dari kecepatan larutan tertinggi yaitu 40 rpm dengan nilai 1.2624 mmy. Kata Kunci : MIG Weld, Kadar Garam, Temperatur Air laut, Kecepatan Air Laut, Laju Korosi. ABSTRACT Indonesia is an archipelagic country whose long coastline reaches 95,181 km. Indonesia is a developing country, especially in the maritime world. Shipbuilding need good quality material and welding especially ship hull. One type of aluminum used in ship construction is aluminum 5083. GMAW welding process is more efficient for aluminum metal. Ship material is often immersed in wet environments (seawater). The seawater environment is very corrosive, so it does not close the possibility of corrosion and every different area of marine environment also has different corrosion rate. The purpose of this research is to know the influence of salinity, temperature, sea water velocity and the relationship of these three variables to the corrosion resistance of aluminum weld metal 5083 butt joint MIG weld. The test method used was linear polarization test with NaCl solution. Based on the linear polarization tafel graph, the temperature, salt concentration and flow rate of the environment influenced the corrosion rate. The higher temperature, the higher corrosion rate, this is proved by the highest corrosion rate value obtained by the highest temperature 40 o C with the value 0.19984 mmy. While the higher salt content, the higher corrosion rate, this is proved by the highest corrosion rate value obtained by the highest salinity 15% with a value of 0.23852 mmy. And the higher the speed the higher the corrosion rate, this is proved by the highest corrosion rate value obtained by the highest liquid velocity 40 rpm with a value of 1.2624 mmy. Keywords: MIG Weld, Salt Content, Sea Water Temperature, Sea Water Speed, Corrosion Rate

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 06:02
Last Modified: 05 Oct 2018 06:02
URI: http://repository.ppns.ac.id/id/eprint/1339

Actions (login required)

View Item View Item