ANALISA VARIASI KUAT ARUS PADA PROSES PENGELASAN SMAW TERHADAP STRUKTUR MIKRO, NILAI HARDNESS DAN FERRITE CONTENT PADA MATERIAL FERRITIC STAINLESS STEEL

Hadidi, Mohammad Danny (2017) ANALISA VARIASI KUAT ARUS PADA PROSES PENGELASAN SMAW TERHADAP STRUKTUR MIKRO, NILAI HARDNESS DAN FERRITE CONTENT PADA MATERIAL FERRITIC STAINLESS STEEL. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Dalam proses pengelasan perlu diperhatikan beberapa parameter proses pengelasan yang berhubungan dengan kualitas hasil las seperti tegangan dan arus yang digunakan, dengan adanya pengaruh variasi kuat arus akan memberikan heat input yang berbeda pada daerah HAZ dan weld metal sehingga mechanical properties dari material setelah dilakukan pengelasan akan berbeda pula. Dalam penelitian ini menggunakan material 3Cr12 yang termasuk dalam type ferritic stainless steel, dengan menggunakan elektroda AWS A5.4 E316-17 yang berdiameter 2.6 mm. Jenis proses pengelasan yang digunakan adalah Shielded Metal Arc Welding (SMAW). Dengan variasi kuat arus 55A, 70A, dan 85A. pengujian yang dilakukan berupa uji Struktur mikro, kekerasan dan ferrite content. Berdasarkan hasil pengujian didapatkan Penggunaan ampere yang tinggi dapat berpengaruh terhadap nilai kekerasannya, semakin tinggi ampere yang digunakan maka semakin tinggi nilai kekerasan. nilai kekerasan tertinggi berada didaerah HAZ sebesar 380,69 HVN, hal ini dikarenakan setelah proses pengelasan pada daerah HAZ akan terbentuk struktur martensite dan carbide presipitation yang menyebabkan kekerasannya meningkat. Untuk daerah weld metal kekerasan yang paling besar berada pada penggunaan kuat arus yang tinggi sebesar 200,81 HVN, ini disebabkan semakin besar penggunaan kuat arus akan menghasilkan struktur ferrite. Hasil pengujian kandungan ferrite dengan menggunakan ferrite scope didapatkan penggunaan kuat arus yang tinggi akan meningkatkan kandungan ferrite. Kata kunci : Ferritic Stainless Steel, 3Cr12, SMAW, ferrite content, dan Hardness. ABSTRACT In the welding prosses. It is important to consider some welding process parameter which are related to welding result quality, like the used voltage and the current. With the influence of current capacity, there will be different heat input in HAZ area and weld metal so, the mechanical properties of the material will also be different after the welding process. In the research, metal 3Cr12 which is one of ferritic stainless steel type is used, by using electrode AWS A5.4 E316L-17 which has 2.6 mm diameter. The type of used weld ing process is Shielded Metal Arc Welding (SMAW). Using 55A, 70A, and 85A, current capacity variance. It is conducted some testing, which are micro structure testing, hardness testing, and ferrite content testing. Based on the test result, it is concluded that the high ampere usage can effect the hardness value. The higher the used ampere, the higher the hardness value. The highest obtained hardness value in the HAZ area is 380,69 HVN. This is caused by formation of martensite and carbide presipitation structure in the welding process in HAZ area which made the hardness increased. The highest hardness value in the weld metal area is obnated at the 200,81 HVN high current usage. That was by the high current usage that will produced ferrite structure. The result of ferrite compositionusing ferrite scope shows that the high current usage will increase the ferrite composition. Keywords : Ferritic Stainless Steel, 3Cr12, SMAW, ferrite content, and Hardness.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 05:55
Last Modified: 05 Oct 2018 05:55
URI: http://repository.ppns.ac.id/id/eprint/1336