PENGARUH SUHU PWHT, HOLDING TIME DAN MEDIA PENDINGIN TERHADAP SIFAT MEKANIK SA-335 P-91 DENGAN METODE TAGUCHI

PRIATMAJA, EKA PRADANA (2017) PENGARUH SUHU PWHT, HOLDING TIME DAN MEDIA PENDINGIN TERHADAP SIFAT MEKANIK SA-335 P-91 DENGAN METODE TAGUCHI. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Post Weld Heat Treatment (PWHT) adalah salah satu proses perlakuan panas yang dilakukan setelah proses pengelasan, tujuan dilakukan proses PWHT adalah untuk mengurangi tegangan sisa setelah proses pengelasan. Setiap material akan mengalami perubahan struktur setelah proses pemanasan dan pendinginan. Cara untuk mengembalikan struktur material seperti semula atau bahkan lebih baik, dapat dilakukan pemanasan dengan suhu dan holding time tertentu. Analisa optimasi ini diharapkan dapat menghasilkan parameter terbaik. Parameter yang dianalisa adalah Suhu PWHT, holding time dan media pendingin. Sedangkan level yang digunakan dalam masing-masing parameter yaitu 2 (dua) level. Pada Suhu PWHT yaitu 650°C dan 750°C, Holding Time selama 20 menit dan 40 menit, dan media pendingin dilakukan di dalam furnace dan pada suhu ruangan. Pengolahan data dengan tingkat kepercayaan 90% dan dibandingkan dengan software Minitab 1.6. Hasil analisa dan pengolahan data didapatkan parameter yang berpengaruh terhadap kekerasan material dan Tensile Strength dengan kontribusi sebagai berikut: Pada Base Metal media pendinginan furnace sebesar 50,04%, Suhu PWHT 650ºC sebesar 30,14%, dan holding time 40 menit sebesar 1,13%. Pada HAZ media pendinginan furnace sebesar 46,85%, suhu PWHT 750ºC sebesar 25,14%, dan Holding Time 40 menit sebesar 35,42%. Pada Weld Metal Media Pendinginan Furnace sebesar 50,04%, Suhu PWHT 650ºC sebesar 30,14%, dan Holding Time 20 menit sebesar 1,13%. Pada Tensile Test media pendinginan udara sebesar 3%, Holding Time 650% sebesar 16% dan Holding Time 20 menit sebesar 2% Kata Kunci: Post Weld Heat Treatment, Metode Taguchi, Daerah Hardness, Tensile Test. ABSTRACT Post Weld Heat Treatment is one of the heat treatment process which is done after welding process. The purpose of PWHT process is to reduce residual stress after welding process. Each Material will through structural changes after heating and cooling process. The way to restore the material structure as before or even better, can be heated with certain temperature and holding time. Optimization analysis is expected to produce the best parameters. The parameters analyzed were PWHT Temperature, Holding Time and Cooling Media. While the level used in each parameter is 2 (Two) levels. At PWHT Temperature of 650 ° C and 750 ° C, Holding Time for 20 minutes and 40 minutes, and Cooling Media is carried out in the furnace and at room temperature. Data processing with 90% confidence level and compared with Minitab software 1.6. The result of analysis and data processing got the parameters which influence to material hardness and Tensile Strength with contribution as follows: At Fase Metering Media Furnace at 50,04%, Temperature PWHT 650ºC 30,14%, and Holding Time 40 minutes equal to 1,13 %. At HAZ Media Cooling Furnace equal to 46,85%, Temperature PWHT 750ºC equal to 25,14%, and Holding Time 40 minute equal to 35,42%. In Weld Metal Media Refrigeration Furnace at 50.04%, PWHT Temperature 650ºC of 30.14%, and Holding Time 20 minutes at 1.13%. In Tensile Test Air Cooling Media by 3%, Holding Time 650% by 16% and Holding Time 20 minutes at 2%. Keywords: Post Weld Heat Treatment, Taguchi Method, Hardness Area, Tensile Test.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 05:30
Last Modified: 05 Oct 2018 05:30
URI: http://repository.ppns.ac.id/id/eprint/1329

Actions (login required)

View Item View Item