PENGARUH MEDIA PENDINGIN DAN SUHU PREHEATING PADA DISSIMILAR MATERIAL BISPLATE 400 DENGAN A 36 TERHADAP NILAI HARDNESS STRUKTUR MIKRO DAN MAKRO

AMINUDIN, MUH. ADE (2017) PENGARUH MEDIA PENDINGIN DAN SUHU PREHEATING PADA DISSIMILAR MATERIAL BISPLATE 400 DENGAN A 36 TERHADAP NILAI HARDNESS STRUKTUR MIKRO DAN MAKRO. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Project rom bin atau bak penampung hasil tambang emas adalah salah satu hasil produksi PT.X yang saat itu sedang dalam proses pengerjaan. Hal yang menjadi perhatian adalah proses pemanasan awal serta aplikasi media pendingin kapur pada material wear resistant bisplate 400. Pada penelitian ini digunakan suhu pemanasan awal 773 ºC dengan variasi media pendingin kapur, pasir dan udara untuk proses drilling, serta preheating 50 ºC dan 75 ºC sebelum pengelasan dapat mempengaruhi nilai hardness, struktur mikro dan makro. Proses las shielded metal arc welding (SMAW) dengan jenis sambungan plug. Data nilai hardness yang didapatkan, diolah dengan metode Analysis Of Variance (ANOVA). Metode ANOVA digunakan untuk mengetahui pengaruh variable yang digunakan. Hasil analisa uji hardness menggunakan metode ANOVA didapatkan nilai signifikansi dari variabel media pendingin kemudian preheat pada HAZ. Dari data uji makro didapatkan perbedaan lebar HAZ dari suhu preheating yang di aplikasikan, semakin tinggi suhu preheating daerah HAZ semakin lebar begitu pula sebaliknya. Dari data uji mikro didapatkan laju pendinginan dari setiap media pendingin yang membuat perbedaan perubahan struktur material. Semakin lambat laju pendinginan membuat struktur material lebih lunak. Kata Kunci: Pemanasan awal, media pendingin, preheating, hardness, mikro dan makro. ABSTRACT Project rom bin or container of gold mining result is one of PT.X production which at that time is in the process of workmanship. Of particular concern is the initial heating process and the application of lime cooling media to the material wear resistant bisplate 400. In this study the initial heating temperature of 773 ºC with variation of lime, sand and air cooling medium for the drilling process, as well as preheating 50 ºC and 75 ºC before welding can affect hardness value, micro structure and macro. The process of shielded metal arc welding (SMAW) welding with plug type connection. Hardness value data obtained, processed by Analysis Of Variance (ANOVA) method. ANOVA method used to determine the effect of variables. Result of hardness test analysis using ANOVA method got significance value from variable of cooling media then preheat at HAZ. From the macro test data obtained differences in HAZ area from preheating temperatures that are applied, the higher the preheating temperature of the HAZ area wider and vice versa. From the micro test data obtained cooling rate of each cooling medium that makes the difference of material structure changes. The slower the cooling rate makes the material structure softer. Keywords : Initial heating, cooling, preheating, hardness, micro and macro.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 05:26
Last Modified: 05 Oct 2018 05:26
URI: http://repository.ppns.ac.id/id/eprint/1328