PERHITUNGAN FATIGUE LIFE PADA MATERIAL EXISTING USED PIPE API 5L GRADE B DENGAN MENGGUNAKAN GRAIN SIZE DAN METODE ELEMEN HINGGA

Khasanah, Uswatun (2017) PERHITUNGAN FATIGUE LIFE PADA MATERIAL EXISTING USED PIPE API 5L GRADE B DENGAN MENGGUNAKAN GRAIN SIZE DAN METODE ELEMEN HINGGA. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Remaining Life merupakan waktu sisa material tersebut masih layak digunakan. Karena dalam pembahasan kali ini adalah tentang prediksi kelayakan pipa bekas, Sehingga harus diketahui untuk nilay cycle material tersebut. Dan selain melakukan prediksi remaining life, untuk mengetahui kelayakan pipa tersebut yang harus dilakukan adalah dengan melihat nilai mechanical properties dari Material Existing Used Pipe dan juga ketebalan minimal sesuai standar. Pada penelitian ini material API 5L Gr.B tetap utuh tanpa dilakukan pengelasan, dan material yang digunakan adalah perbandingan new pipe dan existing used pipe. Pengujian yang akan dilakukan adalah pengujian tarik, metallografi dan simulasi menggunakan software ANSYS untuk mengetahui remaining life pipa tersebut. Sedangkan untuk nilai cycle dilakukan perbandingan antara menggunakan software ansys dan menggunakan struktur mikro. Dari Hasil yang didapat dalam penelitian ini adalah nilai kuat tarik material existing used pipe, dengan nilai σ yield sebesar 336.40 Mpa dan σ ultimate sebesar 475.78 Mpa. Sehingga untuk analisa menggunakan software ansys menggunakan nilai kuat tarik, sedangkan untuk struktur mikro menggunakan perhitungan struktur. Sehingga tekanan yang digunakan adalah untuk perbandingan menggunakan dua analisa tersebut. Sehingga setelah dianalisa nilai cycle pada tekanan 550 Psi, 600 Psi, 650 Psi, dan 700 Psi untuk new pipe memiliki nilai cycle yang lebih besar dari pada existing used pipe Hal tersebut dikarenakan ketebalan untuk new pipe lebih tebal dari existing used pipe, sehingga semakin besar pula nilai remaining life nya. Dan nilai cycle untuk tekanan 700 Psi adalah 8.34E+07, sehingga masih layak digunakan sesuai dengan jurnal acuan. KATA KUNCI : remaining life, software ANSYS,mechanical properties, existing used pipe API 5L Gr.B ABSTRACT Remaining Life is the remaining time of the material is still feasible to use. Because in this discussion is about the prediction of the feasibility of used pipes, So it must be known for the nilay cycle of the material. And besides predicting the remaining life, to know the feasibility of the pipe that must be done is to see the value of mechanical properties of Material Existing Used Pipe and also the minimum thickness according to the standard. In this study the 5L Gr.B API material remains intact without welding, and the material used is the comparison of new pipe and the existing used pipe. Tests to be performed are tensile testing, metallography and simulation using ANSYS software to find out the remaining life of the pipe. As for the value of the cycle made a comparison between using ansys software and using microstructure From the results obtained in this research is the value of tensile strength of existing used pipe material, with a yield value of 336.40 MPa and σ ultimate of 475.78 MPa. So for the analysis using ansys software using tensile strength value, while for micro structure using structure calculation. So the pressure used is for comparison using two such analyzes. So after analyzing the cycle value at 550 Psi, 600 Psi, 650 Psi, and 700 Psi for new pipe has cycle value greater than the existing used pipe This is because thickness for new pipe is thicker than the existing used pipe, Also the value of its remaining life. And the cycle value for the 700 Psi pressure is 8.34E + 07, so it is still feasible to use in accordance with the reference journal. KEYWORDS: remaining life, ANSYS software, mechanical properties, existing used pipe API 5L Gr.B

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 05:19
Last Modified: 05 Oct 2018 05:19
URI: http://repository.ppns.ac.id/id/eprint/1326

Actions (login required)

View Item View Item