ANALISA VARIASI INTERPASS TEMPERATUR PADA MATERIAL A 537 CLASS 1 TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK UNTUK SHELL AMMONIA STORAGE TANK DI BANGGAI AMMONIA PLANT PROJECT

Rochman, Mochammad Ainur (2017) ANALISA VARIASI INTERPASS TEMPERATUR PADA MATERIAL A 537 CLASS 1 TERHADAP STRUKTUR MIKRO DAN SIFAT MEKANIK UNTUK SHELL AMMONIA STORAGE TANK DI BANGGAI AMMONIA PLANT PROJECT. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Salah satu variabel dalam pengelasan adalah interpass temperatur. Pada proyek pengerjaan suatu produk tangki yang mencapai suhu oprasional -75°C dengan pengelasan banyak para welder yang tidak memperhatikan akan hal ini, dengan tujuan pekerjaan yang cepat selesai. Dengan interpass temperatur tinggi, mechanical properties suatu material akan berubah. Dalam penelitian ini menggunakan material A 537 Class 1 dengan ukuran dimensi 150 mm x 200 mm x 18,2 mm dengan sambungan butt joint single groove. Menggunakan proses pengelasan SMAW (Shielded metal arc welding) dengan menggunakan variasi suhu interpass temperatur 150°C, 200°C dan 250°C. Untuk mendapatkan hasil struktur mikro, kekerasan, dan ketangguhan dilakukan pengujian struktur mikro, pengujian kekerasan dan pengujian impak. Dari hasil penelitian ini dapat diketahui bahwa proses pengelasan yang menggunakan suhu interpass 150°C diperoleh nilai kekerasan tertinggi yaitu sebesar 244,93 HVN yang terletak pada HAZ, 227,37 HVN terletak pada weld metal, dan 175,83 HVN pada base metal. Dari segi struktur mikro mengalami perubahan semakin halus, dan dari segi pengujian impak menghasilkan penurunan nilai ketangguhan sebesar 34,37 J pada daerah weld metal dan 66,37 J pada daerah HAZ. Semakin rendah interpass temperatur maka nilai ketangguhan akan semakin menurun. Kata Kunci : SMAW, A537 Class 1, interpass temperatur, kekerasan ketangguhan, struktur mikro. ABSTRACT One of the variables in welding is temperature interpass. In the work project of a tank product that reaches an oprational temperature of -75 ° C with welding many welders are not paying attention to this, with the aim of a rapid work completed. With high temperature interpass, mechanical properties of a material will change In this study using A 537 Class 1 material with dimensions of 150 mm x 200 mm x 18.2 mm with single groove butt joint. Using SMAW (Shielded metal arc welding) welding process by using temperature variation of interpass temperature 150 ° C, 200 ° C and 250 ° C. To obtain the results of microstructure, hardness, and toughness is done metallographic testing of microstructure, hardness testing and impact testing. From the results of this research can be seen that the welding process using interpas temperature 150 ° C obtained by the highest hardness value of 244.93 HVN located at HAZ, 227.37 HVN located in weld metal, and 175.83 HVN on base metal. In terms of microstructure the changes are more refined, and in terms of impact testing resulted in a decrease in toughness value of 34.37 J in the weld metal region and 66.37 J in the HAZ area. The lower the interpass temperature the toughness value will decrease. Keywords: SMAW, A537 Class 1, interpass temperature, hardness, toughness, micro structure.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 05:16
Last Modified: 05 Oct 2018 05:16
URI: http://repository.ppns.ac.id/id/eprint/1325

Actions (login required)

View Item View Item