ANALISA MULTIPLE REPAIR PADA PENGELASAN A-537 CLASS 1 TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO

Wijaya, Rony (2017) ANALISA MULTIPLE REPAIR PADA PENGELASAN A-537 CLASS 1 TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Pada perusahaan tempat OJT dalam pengerjaan project tangki amonia dimana memiliki suhu operasional -50 C. Material yang digunakan dalam pembuatan tangki tersebut adalah A-537 Class 1, proses las yang digunakan adalah SAW. Dalam proses pengelasan di lapangan terjadi cacat dan dilakukan repair. Namun repair yang dilakukan tidak hanya sekali tetapi berulang-ulang. Sehingga mengakibatkan masukan panas yang cukup besar. Penelitian ini dilakukan dengan cara melakukan pengelasan pada material A-537 class 1 menggunakan proses las SAW dan dilakukan proses repair menggunakan metode gouging dan grinding dan proses las yang digunakan adalah proses las SMAW. Repair dilakukan sebanyak 3 kali sehingga ada 4 variasi yaitu tanpa repair, 1x repair, 2x repair dan 3x repair. Pada semua variasi dilakukan pengujian struktur mikro, kekerasan dan juga ketangguhan. Berdasarkan analisa yang telah dilakukan, semakin banyak proses repair yang dilakukan menyebabkan ukuran butir semakin kecil dan prosentase fasa pearlite semakin tinggi. Pada pengujian kekerasan nilainya semakin tinggi seiring banyaknya proses repair. Berbeda dengan pengujian ketangguhan semakin banyak proses repair yang dilakukan menyebabkan nilai ketangguhan semakin rendah. Kata Kunci: Repair,SAW, SMAW, gouging, uji kekerasan, uji ketangguhan dan uji mikro, pearlite ABSTRACT In the company where OJT is in the work of the ammonia tank project which has an operational temperature of -50 C. The material used in the manufacture of the tank is A-537 Class 1, the welding process used is SAW. In the welding process in the field there is a defect and performed repair. But the repair is done not only once but repeatedly. So as to result in a considerable heat input. This research is done by welding on A-537 class 1 material using SAW welding process and repair process using gouging and grinding method and welding process used is SMAW welding process. Repair is done 3 times so there are 4 variations that is without repair, 1x repair, 2x repair and 3x repair. In all variations, microstructure test, hardness test and impact test. Based on the analysis that has been done, the more the repair process is done causing smaller grain size and higher pearlite phase percentage. In hardness testing the value of hardness is increase as the number of repair process. Diferent with the impact test, more the repair process performed causing the toughness value decrease. Kata Kunci: Repair,SAW, SMAW, gouging, Impact, Hardness, metallography test, pearlite

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id