ANALISA PELAKUAN TEKNIK TEMPER BEAD WELDING PADA PENGELASAN PIPA MAINSTEAM BOILER MATERIAL SA 335 P12 SEBAGAI PENGGANTI PWHT TERHADAP TOUGHNESS, HARDNESS DAN STRUKTUR MIKRO

Putra, Aldo Riskiyana (2017) ANALISA PELAKUAN TEKNIK TEMPER BEAD WELDING PADA PENGELASAN PIPA MAINSTEAM BOILER MATERIAL SA 335 P12 SEBAGAI PENGGANTI PWHT TERHADAP TOUGHNESS, HARDNESS DAN STRUKTUR MIKRO. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Teknologi dalam pengelasan sangat berkembang dengan pesat dimana untuk memperbaiki hasil pengelasan yaitu dilakukan proses Post Weld Heat Treatment (PWHT), yang juga bertujuan untuk mengurangi nilai residual stress akibat dari proses pengelasan. Tetapi proses PWHT sangat mahal sehingga ada metode lain yang bisa menggantikan proses PWHT yaitu dengan metode pengelasan Temperbead Welding(TBW). Hal tersebut berkaitan dengan mahalnya harga proses PWHT dalam dunia industri jika barang yang akan di PWHT seperti pipa Mainsteam dan pipa dengan ketebalan di atas 16 mm ,. Biasanya dalam pembuatanya menggunakan material SA 335 P12 yang memang diperuntukan untuk high-temperature servis dan harus mempunyai nilai keamanan yang tinggi dengan menggunakan perlakuan PWHT. Hasil yang didapat dari peneli t ian ini adalah dilihat dari struktur mi kro pada PWHT dan half bead technique yang terj adi pada daerah HAZ menjadi butiran halus. Sedangkan pada consistent layer technique menjadi butiran besar Jika dihubungkan dengan nilai kekerasan yang sama pada daerah HAZ. Dengan rata-rata nilai kekerasan pada PWHT 237,28 HVN, pada half bead technique 237,85 HVN, pada consistent layer technique 253,21 HVN. Hal tersebut terlihat sekali selisih nilai kekerasann ya pada proses half bead technique sangat kecil. Sedangkan pengujian impact pada suhu ruangan terlihat sekali nilai impact pada proses PWHT jika dibandingkan dengan nilai impact antara PWHT 1,59 J/mm 2 dan consistent layer technique 1,50 J/mm 2 dengan selisih 0,09 J/mm 2 . Sedangkan untuk half bead technique nilai impactnya diatas nilai consistent layer technique. Kata-kata kunci : temper bead welding,PWHT, consistent layer technique, half bead technique ABSTRACT Welding technology of repair technique is developing more rapidly nowadays. One of that repair technique is Post Weld Heat Treatment (PWHT) that aims to decreasing the number of residual stress due to welding process. But the cost for PWHT process is so much expensive, so it needs another technique that can replace PWHT process in cheaper cost, which is Temperbead Welding Technique (TBW). This replacement is also due to the effectively of the process to be done on material with the thickness exceed 16mm and to the certain material for high-temperature service as SA 335 P12 for its safety value. The tests that will conduct for this research is micro structure test, impact test, and also hardness test. And the result of those three tests will be determining which one of the repair technique that can be a replacement of PWHT process. The result of this research can be seen from the micro structure of PWHT specimen and Half bead technique on HAZ area which shown as a fine grain. While on consistent layer technique the micro structure shown as a coarse grain. Based on the hardness test result, the highest hardness value coming from HAZ area. The average hardness value of PWHT is 237.28 HVN, on half bead technique is 237.85 HVN, and on c o n s i s t e n t layer technique is 253.21 HVN. While on impact test that conducted in room temperature explain clearly that impact value for PWHT specimen is 1,59 J/mm 2 and for consistent layer technique specimen is1,50 J/mm 2 So from those three tests that can be a placement of PWHT is half bead technique. Keyword : temper bead welding,PWHT, consistent layer technique, half bead technique.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 05:01
Last Modified: 05 Oct 2018 05:01
URI: http://repository.ppns.ac.id/id/eprint/1320

Actions (login required)

View Item View Item