PENGARUH MULTIPLE REPAIR MENGGUNAKAN ELECTRODE GOUGING PADA MATERIAL KI-A TERHADAP NOTCH TOUGHNESS DAN FRACTURE TOUGHNESS SERTA STRUKTUR MIKRO

Mujianto, M. Defri (2017) PENGARUH MULTIPLE REPAIR MENGGUNAKAN ELECTRODE GOUGING PADA MATERIAL KI-A TERHADAP NOTCH TOUGHNESS DAN FRACTURE TOUGHNESS SERTA STRUKTUR MIKRO. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Proses gouging yang dilakukan sering kali tidak memperhatikan faktor-faktor yang dapat mempengaruhi hasil dari proses pengelasan maka dari itu banyak proses repair dengan metode gouging banyak menimbulkan cacat pada material pengelasan. Cacat yang biasanya terjadi yaitu undercut, slag inclusion hingga porosity. Penenlitian ini dilakukan menggunakan 3 metode multiple repair gouging. Proses pengelasan yang digunakan yaitu proses pengelasan SMAW dan material yang digunaakan yaitu material BKI grade A. Penelitian ini dilakukan dengan mengacu pada hasil pengujian impact, three point bending dan struktur mikro. Dari hasil pengujian didapatkan bahwa semakin banyak frekuensi repair gouging yang dilakukan maka semakin kecil nilai impact, semakin kecil pula nilai fracture toughness (Kic), dan semakin tinggi nilai kekerasan hal ini ditandai dengan adanya persentase pearlite pada material khususnya pada daerah weld metal. Kata kunci: multiple repair, gouging, notch toughness, fracture toughness, struktur mikro ABSTRACT Gouging process usually conduct denying some factors that will be affect the welding result which is it makes many defect appears on weld metal. Those defects are undercut, slag inclusion and porosity. This research will be conduct with 3 method variations of multiple gouging repair. Welding process will be use is SMAW and the material used is BKI material grade A. And this research based on the research of impact test, three point bending testand micro structure of material. From the tests turns out that the higher frequency of gouging repair, the lower the impact value, the lower fracture toughness (Kic) value and the higher the value of violence this is indicated by the percentage of pearlite of the material especially in weld metal. Keyword: multiple repair, gouging, notch toughness, fracture toughness, structure micro

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 03:50
Last Modified: 05 Oct 2018 03:50
URI: http://repository.ppns.ac.id/id/eprint/1315

Actions (login required)

View Item View Item