ANALISA VARIASI KECEPATAN ALIRAN FLUIDA PADA PROSES PENGELASAN GTAW MATERIAL SA 106 GRADE B DENGAN SA 312 TP 304L TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN DAN FERRITE CONTENT

AFANDI, MOHAMMAD YUSUF (2017) ANALISA VARIASI KECEPATAN ALIRAN FLUIDA PADA PROSES PENGELASAN GTAW MATERIAL SA 106 GRADE B DENGAN SA 312 TP 304L TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN DAN FERRITE CONTENT. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Pada Plant FA dilakukan proses pergantian pipa,dengan mengunakan metode repair yang tidak benar. Dimana salah satunya pada sambungan proses pengelasan beda material (dissimilar joint). Pergantian pemasangan pipa ini dikerjakan dengan melakukan proses pengelasan tanpa menghentikan aliran air dari proses produksi, Sehingga mengakibatkan pendinginan cepat ( quenching). Dalam penelitian ini menggunakan material SA 106 Grade B NPS 4 sch 40 dengan ketebalan 6 mm dengan SA 312 Tp 304L NPS 4 sch 40 dengan ketebalan 6 mm. Proses pengelasan dilakukan dengan metode GTAW dengan menggunakan elektroda ER309L dengan memvariasikan flow rate 0 LPM (Liter Per Minute), 4 LPM (Liter Per Minute), 5,5 LPM (Liter Per Minute) dan 7 LPM (Liter Per Minute). Pada pengujian struktur mikro untuk daerah yang diambil tidak terjadi perubahan bentuk butir yang terlihat kecuali pada HAZ Carbon Steel terjadi perbedaan. Dari data uji kekerasan, dengan semakin cepat flow rate hasil kekerasannya semakin meningkat juga. Sedangkan jika di lihat dari data ferrite content semakin cepat flow rate fluida maka hasil ferrite content yang di hasilkan semakin rendah. Hal tersebut di akibatkan oleh adanya kecepatan air yang berbeda dan proses pendinginan cepat (quench) Kata-kata kunci :, Dissimilar welding , Flowrate,in-service pipelines, GTAW ABSTRACT The replacing process in FA plant was conducted in wrong repair method. Which one oof it was on the welding process for dissimilar joint. These pipe replacement was conduct with keep the fluida flow on while the process was on going. Which is these process making the cooling rate is faster or it called quenching. On this research using SA 106 Grade B NPS 4 sch 40 with 6 mm thickness with SA 312 Tp 304L NPS 4 sch 40 with 6 mm thickness. The welding process being used is GTAW by using ER309L electrode. The variations of this research are using flow rate of 0 LPM (Liter Per Minute), 4 LPM (Liter Per Minute), 5,5 LPM (Liter Per Minute) dan 7 LPM (Liter Per Minute). On microstructure test for the area being tested, there were no difference of grain size except on HAZ carbon steel. From the result of hardness test, the faster the flow rate, the higher hardness value. Whereas on ferrite content, the faster the flow rate, the lower the ferrite content. Those the research result caused by the differences of flow rate and cooling rate process. Keywords : Dissimilar welding , Flowrate,in-service pipelines, GTAW

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 03:19
Last Modified: 05 Oct 2018 03:19
URI: http://repository.ppns.ac.id/id/eprint/1306