PENGARUH WELDING PARAMETER RESISTANCE SEAM WELDING TERHADAP KEKUATAN GESER DAN METALLOGRAPHY PADA SAMBUNGAN DISSIMILAR MATERIAL SUS304 DENGAN SS400

ASYHARI, MUCHAMAD (2017) PENGARUH WELDING PARAMETER RESISTANCE SEAM WELDING TERHADAP KEKUATAN GESER DAN METALLOGRAPHY PADA SAMBUNGAN DISSIMILAR MATERIAL SUS304 DENGAN SS400. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK PT X merupakan perusahaan yang bergerak di bidang pembuatan kereta api. Pada proses pembuatan floor direncanakan akan menggunakan material SUS304 dan SS400. Material SUS304 digunakan karena memiliki corrosion resistance yang baik dan SS400 dipilih karena harga murah dan mechanichal propertis yang baik. Penelitian dilakukan untuk mengetahui pengaruh welding parameter resistance seam welding terhadap kekuatan geser dan metallography serta hardeness pada sambungan dissimilar material. Pada penelitian ini base metal di sambung menggunakan mesin seam welding dengan variasi ampere dan welding speed yang dibutuhkan. Ada satu join disetiap variasi dengan penamaan 10k2, 10k3, 11k2, dan 11k3. Pengujian metallograpgy hanya menggunakan makro test baik longitudinal maupun transversal. Kemudian dilanjutkan dengan pengujian geser dan micro hardness vikers. Hasil menunjukkan bahwa pengujian makro terdpat nugget yang terbentuk baik transversal maupun longitudinal. Ukuran nugget berbeda di setiap variasi yang dipakai. Sedangkan dilihat dari uji geser, nugget yang terbentuk menghasilkan nilai yang sesuai dengan standart keberterimaan sehingga nugget memiliki kualitas yang baik. Pada pengujian hardness didapati nilai yang bervariatif sesuai dengan variasi yang digunakan. Kenaikan ampere yang digunakan mengasilkan ukuran nugget, kekuatan geser dan hardness yang tinggi, namun menaikkan kecepatan pengelasan memberikan effect yang sebaliknya pada hasil las-lasan. Kata Kunci : SUS304, SS400, Uji Makro, Uji Geser, Uji Hardness ABSTRACT PT X is a company that works in train producing field of work. On the Floor making process is planned to use material SUS304 and SS400. Material SUS304 is used because of its good corrosion resistance and material SS400 is used because of its low cost and good mechanical properties. This research means to know the influence of welding parameter of resistance seam welding to the shear strength, metallography and hardeness value on dissimilar joint of material. On this research, base metal was joined using seam welding machine with ampere variation and also welding speed. There a single join on every variation that named 10k2, 10k3, 11k2, and 11k3. Metallography test just use macro etch method forboth longitudinal and transversal. Then continue with shear test and mcrohardness. The result show that on macro test there were nugget when it seen from both transversal and longitudinal. The size of nugget is different on every single variation. Meanwhile from the shear test turns out that the nuggets formed is appropriate with the acceptance criteria. On hardness test turns out vary of hardness value among all of variations. The inclining of ampere uses make the increasing of nugget size, shear strength and hardness value, but the inclining of welding speed gave the opposite result.. Key words : SUS304, SS400, Macro test, shear test, hardness test

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 03:15
Last Modified: 05 Oct 2018 03:15
URI: http://repository.ppns.ac.id/id/eprint/1305

Actions (login required)

View Item View Item