ANALISA BACKING GAS H2N2 PADA PENGELASAN SAMBUNGAN MATERIAL STAINLESS STEEL SA 312 TP304 DENGAN PROSES GTAW TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN DAN PITTING CORROSION DI PT GI

PRATAMA, NIBRAS BUDI (2017) ANALISA BACKING GAS H2N2 PADA PENGELASAN SAMBUNGAN MATERIAL STAINLESS STEEL SA 312 TP304 DENGAN PROSES GTAW TERHADAP STRUKTUR MIKRO, NILAI KEKERASAN DAN PITTING CORROSION DI PT GI. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Di PT GI proses pengelasan material stainless steel mengunakan backing gas H 2N2 . Penggunaan H 2N2 sebagai backing gas dapat mempengaruhi kekerasan maupun ketahanan korosi hasil pengelasan. Berkaitan dengan hal tersebut, penelitian ini akan mencoba mencari tahu kebenaran dan memberikan kesimpulan mengenai pengelasan dengan beacking gas H2N2 dengan melihat hasil pengelasan dengan nilai Hardness, mikro struktur dan pitting corrosion. Penelitian ini dilakukan dengan menggunakan material SA 312 type 304 dengan proses pengelasan GTAW. Variasi penggunaan backing gas yaitu H 2N2 20%-80%, 15%-85% dan 5%-95%. Hasil pengujian mikro menunjukan pada spesimen uji dengan penggunaan campuran gas nitrogen yang lebih besar akan terlihat struktur ferite yang lebih banyak. Dari hasil pengujian hardness menunjukan bahwa semakin besar kandungan gas nitrogen yang digunakan maka akan semakin besar pula nilai kekerasan pada hasil pengelasan. Dan hasil pengujian korosi . Menunjukkan laju korosi paling tinggi adalah material yang mengunakan Backing gas H2N2 ( 5%-95%). Kata kunci: Backing gas, H2N2 , kekerasan, corrosion, micro structure ABSTRACT In PT GI, H2N2 use as backing gas for stainless steel welding process. The uses of H2N2 as backing gas may affect the hardness value and the corrosion resistance of weld joint. Based on that issue, this research aims to looking for the proven data and the conclusion about the uses of H 2N2 on welding process through the result of hardness test, micro structure test and pitting corrosion. This research conducted by using SA 312 type 304 material with GTAW process. The variations of backing gas use are H 2N2 20%-80%, 15%-85% and 5%-95%. The micro structure test turns out that on specimen with more Nitrogen gas mixture will increase the ferrite contain. From the hardness test show that the higher the Nitrogen gas is used, the higher the hardness value. And form the corrosion test show that the faster corrosion rate coming from the specimen with H2N2 backing gas for about 5%-95%. Key Words: Backing gas, H2N2 , hardness, corrosion, micro structure

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 05 Oct 2018 02:56
Last Modified: 05 Oct 2018 02:56
URI: http://repository.ppns.ac.id/id/eprint/1296