ANALISIS PERBANDINGAN FILLER METAL DAN PANJANG SOCKET (LAP JOINT) BRAZING PADA SAMBUNGAN TUBE AUSTENITE STAINLESS STEEL 304 DAN COPPER CuFe2P(K65) TERHADAP STRUKTUR MIKRO DAN KUAT TARIK

FAUZI, AHMAD NOOR (2017) ANALISIS PERBANDINGAN FILLER METAL DAN PANJANG SOCKET (LAP JOINT) BRAZING PADA SAMBUNGAN TUBE AUSTENITE STAINLESS STEEL 304 DAN COPPER CuFe2P(K65) TERHADAP STRUKTUR MIKRO DAN KUAT TARIK. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Dalam pembuatan heat exchanger terdapat proses penyambungan komponen tube yang berbeda jenis materialnya, proses penyambungan yang sangat mungkin dilakukan dalam manufacturing heat excahanger adalah proses brazing. Pemilihihan filler metal dan penambahan panjang socket (lap joint) pada proses brazing akan mempengaruhi kualitas sambungan dan kekuatan beban tariknya. Pada penelitian ini proses brazing yang digunakan adalah torch brazing, di lakukan dengan posisi horizontal. Filler yang digunakan adalah AF 319 dan AF 333 dengan konfigurasi panjang socket (lap joint) 5mm, 10mm, dan 15mm. Metode pengujian yang digunakan adalah uji kebocoran, uji metalografi, full section tensile test. Kemudian ditambahkan perhitungan estimasi biaya Dari hasil pengujian dapat disimpulkan bahwa filler AF 333 dengan konfigurasi panjang socket (lap joint) 10mm memiliki kekuatan mekanik yang baik dibanding AF 319, dengan nilai ultimate tensile stress rata-rata 404.94 MPa. Struktur mikro yang dihasilkan pada daerah filler metal memiliki struktur yang berbeda, penyebaran filler metal yang dihasilkan lebih baik AF 333 dibanding AF 319. Jika ditinjau dari segi estimasi biaya AF 333 lebih murah dengan harga sebesar Rp 1.429,-/joint dibanding AF 319 dengan harga Rp 1.819,-/joint Kata kunci : torch brazing, perbandingan filler, panjang socket (Lap jont), uji metallography,uji tarik ABSTRACT In the manufacture of heat exchangers there is a process of connecting tube components of different types of material, the process of joining is very possible in manufacturing heat excahanger is the process of brazing. Filling of filler metal and addition of socket length (lap joint) on the brazing process will affect the quality of the connection and the strength of the tensile load. In this research brazing process used is torch brazing, done in a horizontal position. Filler used is AF 319 and AF 333 with the configuration of the socket (lap joint) 5mm, 10mm, and 15mm. Test method used is leak test, metallographic test, full section tensile test. Then calculated cost estimation From the test results can be concluded that the filler AF 333 with the configuration of the socket (lap joint) 10mm has good mechanical strength compared to AF 319, with ultimate tensile stress value of 404.94 MPa. The microstructure produced in the filler metal area has a different structure, the dispersion of metallized filler produced better AF 333 than AF 319. In terms of estimated cost of AF 333 cheaper with the price of Rp 1.429, - / joint compared to AF 319 with the price Rp 1.819, - / joint Keywords: torch brazing, comparative filler, long socket (Lap jont), metallography test, tensile test

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 04 Oct 2018 07:58
Last Modified: 04 Oct 2018 07:58
URI: http://repository.ppns.ac.id/id/eprint/1293