PERBANDINGAN VARIASI KUAT ARUS PROSES PENGELASAN SMAW MATERIAL SA 36 DENGAN SA 240 304 PADA SAMBUNGAN LAP JOINT TERHADAP TEGANGAN GESER, STRUKTUR MIKRO , DAN FRACTURE TOUGHNESS

Hendratno, Adam Maulana (2017) PERBANDINGAN VARIASI KUAT ARUS PROSES PENGELASAN SMAW MATERIAL SA 36 DENGAN SA 240 304 PADA SAMBUNGAN LAP JOINT TERHADAP TEGANGAN GESER, STRUKTUR MIKRO , DAN FRACTURE TOUGHNESS. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Di PT. Srikaya Putra Mas terdapat permasalahan yang berhubungan dengan pengelasan dissimilar yaitu antara stainless steel dan carbon steel. Dalam kasus ini baja karbon SA 36 disambung stainless steel SA 240 304 di mana kedua material tersebut memiliki mechanical properties, chemical composition, dan perlakuan yang berbeda-beda. Maka dari itu perlu dilakukan analisa yang mendalam menggunakan variasi kuat arus, untuk mencapai kualitas sambungan yang baik, terutama ditinjau dari struktur mikro, tegangan geser dan fracture toughness dari material yang berbeda tersebut. Pada penelitian ini dilakukan 3 variasi kuat arus yaitu 80 A, 120 A dan 150 A. Proses pengelasan yang digunakan yaitu SMAW. Base metal yang digunakan yaitu baja karbon SA 36 dengan tebal 10 mm disambung dengan material stainless steel SA2 40 304 dengan tebal 8 mm, type sambungan lap joint, elektrode yang digunakan yaitu E 309L. Pada setiap variasi kuat arus dilakukan pengujian metalografi (mikro), pengujian geser dan fracture toughness. Hasil penelitian ini menjelaskan bahwa semakin tinggi kuat arus mengakibatkan stainless steel terbentuk fasa ferrite yang semakin banyak. Banyaknya kandunggan ferrite pada stainless steel akan menaikkan nilai kekerasannya. Sedangkan untuk baja karbon semakin tinggi kuat arus fasa yang terbentuk adalah perlit, di mana fasa perlit pada baja karbon akan menaikkan nilai kekerasan dan menurunkan nilai ketangguhan. Untuk hasil dari pengujian geser, pengelasan dengan kuat arus 150 A memiliki nilai USS ( ultimate shear test ) yang paling tinggi. Sementara hasil dari pengujian Three Point Bending menunjukkan nilai fracture toughnes tertinggi terdapat pada pengelasan dengan kuat arus 80 A. Kata kunci : Dissimillar Arc Welding, Material A36, Material SA 240 304L, Kuat Arus, Uji Metalografi, Shear Test, Fracture Toughness. T. Srikaya Putra Mas there are p40 304L, Strong Flow, Metallographic Test,hAt PT. Srikaya Putra Mas there are problems related to welding dissimilar which is between stainless steel and carbon steel. In this case the SA 36 carbon steel is joined with stainless steel SA 240 304 where both materials have different mechanical properties, chemical composition, and treatment. Therefore, it is necessary to carry out in deep analysis using current strength variations, to achieve good connection quality, especially in terms of microstructure, shear stress and fracture toughness of the different materials. In this research, 3 variations of current strength are 80 A, 120 A and 150 A. Welding process which is used is SMAW. Base metal which is used is SA 36 carbon steel with 10 mm thickness is connected with stainless steel material SA2 40 304 with thickness 8 mm, type lap joint, electrode used is E 309L. In each variation of current strength done metallographic (micro) testing, shear testing and fractu re toughness. The results of this study explain that the higher the strong current resulting stainless steel formed ferrite phase more and more. The amount of ferrite on stainless steel will increase the hardness value. As for higher carbon s teels the strong phase currents formed are pearlite, where the pearlite phase in carbon steel will increase the hardness value and decrease the toughness value. For the results of shear testing, the strongest welding current of 150 A has the highest USS (u ltimate shear test) value. While the results of the Three Point Bending test showed the highest fracture toughnes value found in welding with a strong current of 80 A. Keywords: Dissimillar Arc Welding, Material A36, Material SA 240 304L, Strong Flow, Metallographic Test, Shear Test, Fracture Toughness

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 04 Oct 2018 07:56
Last Modified: 04 Oct 2018 07:56
URI: http://repository.ppns.ac.id/id/eprint/1292