PENGARUH TEMPERATUR PREHEAT PADA BUFFER LAYER PENGELASAN DISSIMILAR TEE JOINT MATERIAL SA240- 304L DENGAN A36 TERHADAP PENGUJIAN STRUKTUR MIKRO HARDNESS DAN FERRITE CONTENT.

RIGEL, AHMAD (2017) PENGARUH TEMPERATUR PREHEAT PADA BUFFER LAYER PENGELASAN DISSIMILAR TEE JOINT MATERIAL SA240- 304L DENGAN A36 TERHADAP PENGUJIAN STRUKTUR MIKRO HARDNESS DAN FERRITE CONTENT. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Di PT. X terdapat permasalahan yang berhubungan dengan pengelasan dissimilar yaitu antara stainless steel dan carbon steel. Dalam kasus ini baja karbon A36 disambung stainless steel SA- 240- 304L dimana kedua material tersebut memiliki mechanical properties, chemical composition, dan perlakuan yang berbeda- beda. Untuk material baja karbon memiliki ketebalan lebih dari 25 mm dan terdapat proses penam bahan dimensi ketebalan Buffer layer, sehingga perlu dilakukan perlakuan panas yaitu preheat, akan tetapi untuk material stainless steel perlakuan preheat tidak dianjurkan . Maka dari itu perlu dilakukan analisa yang mendalam menggunakan variasi preheat , untuk mencapai kualitas sambungan yang baik, terutama ditinjau dari struktur mikro, nilai kekerasan dan ferrit content dari material yang berbeda tersebut. Pada penelitian ini dilakukan 3 variasi preheat yaitu no preheat, preheat 79ºC dan preheat 150 ºC proses pengelasan yang digunakan yaitu GTAW dan SMAW. Base metal yang digunakan yaitu baja karbon A36 dengan tebal 25 mm disambung dengan material stainless steel SA240- 304L dengan tebal 12 mm, type sambungan tee joint , f iller dan elektrode yang digunakan yaitu E7018, ER309L dan E308L. Pada setiap variasi preheat dilakukan pengujian mengg unkana, uji metalografi (mikro), hardness test (Vickers) dan ferrite content . Hasil penelitian ini menjelaskan bahwa semakin tinggi temperatur preheat mengakibatkan untuk stainless steel, fasa ferrit akan terbentuk semakin banyak dan didapat kandungan ferrit e tertinggi mencapai 6,2 %, banyaknya kandunggan ferrit pada stainless steel akan menaikkan nilai kekerasannya. Sedangkan untuk baja karbon semakin tinggi temperature preheat fasa yang terbentuk adalah ferrit e, dimana fasa ferrit e pada baja karbon akan menurunkan nilai kekerasan dan ketangguhan . Kata kunci : Dissimilar Arc Welding, Material A36, Material SA- 240-304L, Preheating, Uji Metalografi, Hardness, Ferrite Content . ABSTRACT At PT. X there are problems related to welding dissimilar that is between stainless steel and carbon steel. In this case carbon steel A36 stainless steel SA -240-304L stainless steel which is both of those materials has mechanical properties, chemical composition, and different treatment. For carbon steel material have more than 25 mm thickness and there is an addition thickness dimensions process, buffer layer, which need such an heat treatment called preheat , but for stainless steel material preheat treatm ent is not recommended. Therefore, it is necessary to analyze using preheat variation, to achieve good quality weld join, especially in terms of micro structure, hardness value and ferrite content from different materials. In this research, there are 3 preheat variations, which are no preheat, preheat 79ºC and preheat 150 ºC welding process used is GTAW and SMAW. The base metal used is A36 carbon steel with 25 mm thickness combined with SA240 -304L stainless steel material with 12 mm thickness, tee joint typ e, filler and electrode used are E7018, ER309L and E308L. On every variation of preheat tests were performed using metallographic (micro), hardness test (Vickers) and ferrite content. The results of this study explain that the higher preheat temperature leads to stainless steel, the ferrite phase will form more and get the highest ferrite content reaches 6.2%, and the amount of ferrite content in stainless steel will increase the hardness value. As for the higher carbon steel phase preheat temperature formed is ferrite, where the ferrite phase on carbon steel will reduce the value of hardness and toughness. Keywords: Dissimilar Arc Welding Material, A36 Material, SA-240-304L, Preheating, Metallographic test, Hardness, Ferrite Content .

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 04 Oct 2018 07:37
Last Modified: 04 Oct 2018 07:37
URI: http://repository.ppns.ac.id/id/eprint/1288

Actions (login required)

View Item View Item