ANALISA VARIASI INTERPASS TEMPERATUR DAN JUMLAH LAYER PADA PROSES OVERLAY MATERIAL SA 106 GRADE B TERHADAP MECHANICAL PROPERTIES DAN PITTING CORROSION

Kurniawan, Caesar Anggadika (2017) ANALISA VARIASI INTERPASS TEMPERATUR DAN JUMLAH LAYER PADA PROSES OVERLAY MATERIAL SA 106 GRADE B TERHADAP MECHANICAL PROPERTIES DAN PITTING CORROSION. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Pengelasan tidak dapat dipisahkan dalam dunia industri terutama dunia konstruksi. Dalam pengelasan dikenal teknik overlay atau pelapisan. Teknik yang banyak digunakan pada material tube – tube hingga pipa dengan diameter relativ kecil ini sering digunakan sebagai pelindung material dari korosi. Pengelasan overlay dengan teknik gas tungsten arc welding ( GTAW ) digunakan oleh PT. X pada material carbon steel SA 106 yang digunakan pada konstruksi heat excarge. Overlay menggunakan elektroda 309 dan 316 dimaksudkan untuk meningkatkan sifat ketahanan korosi pada material Dari hasil analisa struktur micro spesimen terlihat struktur dari logam induk atau base metal cenderung padat. Hal ini dikarenakan panas yang diterima selama proses pengelasan menggunakan elektroda 309 dan 316. Struktur yang terbentuk pada layers kedua dengan penggunaan elektroda 309 memilikikandungan ferite yang berbanding lurus dengan interpass temperatur yang digunakan. Kandungan ferite pada penggunaan interpas 200 o c lebih banyak daripada 150 o c. Hasil uji kekerasan spesimen juga meninjukan nilai kekerasan pada layers 2 hingga layer 4 dan 5 juga menunjukan nilai berbanding lurus dengan temperatur transisi yang digunakan. Hal ini dikarenakan kandungan ferite yang lebih besar pada penggunaan temeratur transisi 200 o c daripada 150 o c. Namun laju korosi pada spesimen dimana menggunakan larutan ferite chlorite sebagai media korosif meninjukan nilai laju korosi menurun. Pada proses pengelasan 5 layers laju korosi lebih lecil daripada proses pengelasan dengan 4 layer. Hal ini menunjukan jumlah layer yang digunakan berbanding lurus dengan nilai ketahanan korosi material. Kata kunci : GTAW welding, overlay, micro hardness , struktur micro, dan pitting corrosion ABSTRACT Welding can not be separated in the world of industry, especially the world of construction. In welding is known overlay or coating technique. Techniques that are widely used in tube materials to pipes with small relative diameters are often used as a material protection from corrosion. Welding overlay with Gas Tungsten Arc Welding (GTAW) technique used by PT. X on carbon steel SA 106 material used in heat excarge construction. Overlays using 309 and 316 electrodes are intended to improve the corrosion resistance properties of the material. The use of 316 electrodes which have higher corrosion resistance properties is expected to increase the life of heat excharges From the result of structural analysis of the micro-specimen, the structure of the parent metal or base metal tends to be solid. This is due to the heat received during the welding process using electrodes 309 and 316. The structures formed on the second layers with the use of electrodes 309 have ferite contents that are directly aligned with the temperature interpas used. The ferite content on the 200 o C use interpas is more than 150o C. The specimen hardness test results also show the value of hardness on layers 2 to layers 4 and 5 also shows a value proportional to the transition temperature used. This is due to the greater ferrite content in the use of transition temperatures of 200oc rather than 150o C. However, the corrosion rate on specimens where using ferite chlorite solution as a corrosive medium impinging on the value of corrosion rate decreases. In the welding process 5 layers corrosion rate is smaller than welding process with 4 layers. This shows the number of layers used is directly proportional to the corrosion resistance value of the material. Keyword : GTAW welding, overlay, micro hardness , struktur micro, dan pitting corrosion

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 04 Oct 2018 07:23
Last Modified: 04 Oct 2018 07:23
URI: http://repository.ppns.ac.id/id/eprint/1284