ANALISA CONTROLLED DEPOSITION TECHNIQUE DAN WELD TOE TEMPERING TECHNIQUE SEBAGAI PENGGANTI PWHT PADA PENGELASAN MATERIAL SA-537 Class 2 TERHADAP STRUKTUR MIKRO DAN MECHANICAL PROPERTIES

Apriantoko, Bagus (2017) ANALISA CONTROLLED DEPOSITION TECHNIQUE DAN WELD TOE TEMPERING TECHNIQUE SEBAGAI PENGGANTI PWHT PADA PENGELASAN MATERIAL SA-537 Class 2 TERHADAP STRUKTUR MIKRO DAN MECHANICAL PROPERTIES. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Post Weld Heat Treatment (PWHT) bertujuan untuk menghilangkan tegangan sisa yang terbentuk setelah proses pengelasan. Namun faktanya terkadang PWHT tidak dilakukan pada waktu pengerjaan di lapangan karena beberapa faktor penghambat antara lain, memakan waktu yang lama dan biaya yang mahal. Oleh karena itu perlu adanya solusi untuk menggantikan proses PWHT, yaitu dengan menggunakan teknik Temper Bead Welding. Teknik Temper Bead Welding yang digunakan pada penelitian ini yaitu Controlled Deposition Technique (CDT) dan Weld Toe Tempering Technique (WTT) dan dibandingkan dengan proses pengelasan PWHT temperatur 615 o C dengan holding time selama 2 jam 25 menit. Proses pengelasan semuanya menggunakan proses las SMAW. Pengujian yang digunakan adalah pengujian tensile, pengujian bending, pengujian hardness, pengujian impact, dan pengujian struktur mikro. Hasil dari pengujian struktur mikro menunjukkan bahwa dua teknik Temper Bead Welding menghasilkan bentuk struktur yang halus dan bergaris tajam pada batas butirnya. Sedangkan dari hasil pengujian mechanical teknik Temper Bead Welding metode Controlled Deposition Technique dan Weld Toe Tempering Technique berhasil mendekati hasil dari proses PWHT. Kata kunci : Temper Bead Welding, Controlled Deposition Technique, Weld Toe Tempering Technique, SA-537 Class 2 ABSTRACT Post Weld Heat Treatment (PWHT) aims to remove residual stresses formed after the welding process. But in fact, sometime PWHT does not use in field work because of some factors, such as takes longer time to be done and expensive cost. Because of that, the solution to replace PWHT process is needed. Temper Bead Welding is one of those solutions. The Temper Bead Welding technique used in this research is Controlled Deposition Technique (CDT) and Weld Toe Tempering Technique (WTT) and compared with PWHT welding process temperature 615 o C with holding time for 2 hours 25 minutes. The welding process all use the SMAW welding process. Tests used are tensile test, bending test, hardness testing, impact test, and micro structure testing. The results of the microstructure test show that two Temper Bead Welding techniques produce a smooth and sharply shaped structure on the grain boundary. While the results of mechanical testing techniques Temper Bead Welding Controlled Deposition Technique method and Weld Toe Tempering Technique successfully approached the results of the PWHT process. Keywords: Temper Bead Welding, Controlled Deposition Technique, Weld Toe Tempering Technique, SA-537 Class 2

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Pengelasan
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 04 Oct 2018 07:15
Last Modified: 04 Oct 2018 07:15
URI: http://repository.ppns.ac.id/id/eprint/1282

Actions (login required)

View Item View Item