PENGARUH BESAR SUDUT TEKUK TERHADAP NILAI KEKERASAN DAN STRUKTUR MIKRO MATERIAL ST 37

Dahroni, Dawam (2017) PENGARUH BESAR SUDUT TEKUK TERHADAP NILAI KEKERASAN DAN STRUKTUR MIKRO MATERIAL ST 37. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Penelitian ini bertujuan untuk menganalisa pengaruh proses penekukan menggunakan panas terhadap perubahan kekerasan dan struktur mikro. Spesimen uji yang digunakan adalah plat baja ST 37 yang diperlakukan penekukan panas menggunakan tiga macam sudut penekukan yaitu 30 0 , 60 0 , dan 90 0 . Pengujian yang dilakukan terhadap spesimen adalah pengujian kekerasan dan pengujian struktur mikro. Hasil pengujian kekerasan menunjukkan bahwa nilai kekerasan tertinggi terletak pada spesimen yang mengalami bending panas dengan sudut tekuk 90 0 yaitu sebesar 140.10 HBW. Karena spesimen bending panas dengan sudut tekuk 90 0 mengalami deformasi plastis yang paling besar, sehingga memiliki nilai kekerasan tertinggi. Hasil pengujian struktur mikro menunjukkan bahwa fasa yang terbentuk pada proses penekukan panas sudut 30 0 ,60 0 , dan 90 0 adalah ferrite dan pearlite. Kata kunci: Proses Penekukan, Perlakuan Panas, Pengujian Kekerasan, Pengujian Struktur Mikro. ABSTRACT This research aimed to analyze the effect of the bending process by heating towards the change of the hardness value and microstructure. The material which is applied in this research is ST 37 steel plate that will be treated by heat-bending process within three kinds of bend-angle, they are 30 0 , 60 0 , and 90 0 . This research will use hardness test and microstructure test. The results of the hardness test shows that the highest hardness value is in the specimen within bend-angle of 90 0 which has 140.10 HBW in hardness value. Due to the highest plastic deformation in it, so it has the highest hardness value of all bending specimen. The result of the microstructure test shows that the result of the phase within the bending process by heating in bend-angle of 30 0 ,60 0 , and 90 0 is ferrite and pearlite. Keywords :Bending Process, Heat Treatment, Hardness Test, Microstructure Test

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Jurusan Teknik Bangunan Kapal > Teknik Bangunan Kapal
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 22 Sep 2018 04:10
Last Modified: 22 Sep 2018 04:10
URI: http://repository.ppns.ac.id/id/eprint/1195