PEMANFAATAN LIMBAH SLAG SEBAGAI SUBSTITUSI AGREGAT KASAR DAN DEBU EAF (ELECTRIC ARC FURNACE) SEBAGAI SUBSTITUSI SEMEN DALAM PEMBUATAN BETON DI PERUSAHAAN PELEBURAN BAJA

Dewi, Vesti Triana (2017) PEMANFAATAN LIMBAH SLAG SEBAGAI SUBSTITUSI AGREGAT KASAR DAN DEBU EAF (ELECTRIC ARC FURNACE) SEBAGAI SUBSTITUSI SEMEN DALAM PEMBUATAN BETON DI PERUSAHAAN PELEBURAN BAJA. Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK Limbah slag dan debu EAF merupakan limbah sisa peleburan baja. Perusahaan peleburan baja ini menghasilkan slag sebanyak 6480 ton/tahun dan debu EAF mencapai volume 1680 m 3 /tahun. Limbah slag dikumpulkan kemudian diserahkan kepada pihak ketiga, namun debu EAF hanya ditimbun dalam tanah.Berdasarkan wawancara langsung pada pekerja, diketahui bahwa semua pekerja memiliki keluhan sakit yang disebabkan oleh adanya limbah-limbah tersebut.Oleh karena itu, dilakukan pemanfaatan limbah menjadi beton. Penelitian ini memiliki tujuan untuk mengetahui kandungan logam berat limbah slag dan debu EAF dengan uji SEM, pengaruh penambahan limbah slag dan debu EAF terhadap nilai kuat tekan, dan mengetahui kelayakan beton ringan terhadap lingkungan melalui uji TCLP. Penelitian yang dilakukan meliputi pengujian material, perhitungan mix design, pembuatan beton, pengujian kuat tekan, pengukuran berat jenis, dan pengujian TCLP. Campuran yang digunakan adalah slag sebesar 0%, 10%, 20%, 30% dan 40% dari berat agregat kasar dan debu EAF sebesar 0% dan 10% dari berat semen. Berdasarkan hasil penelitian, kandungan logam berat yang ada berdasarkan uji SEM pada limbah slag antara lain Fe (47,94%); Cr (0,2%); Mn (1,618%) dan debu EAF antara lain Fe (32,443%); Zn (31,215%); Mn (4,265%). Untuk nilai kuat tekan beton normal adalah 36,279 MPa dari rencana sebesar 30 MPa, sedangkan nilai kuat tekan debu dengan substitusi slag dan debu EAF mengalami penurunan berturut-turut adalah 35,677 MPa; 35,491 MPa; 35,237 MPa; 35,190 MPa. Pengujian TCLP menyatakan bahwa produk yang dihasilkan aman bagi lingkungan sesuai PP No. 101 Tahun 2014. Kata Kunci: Slag, Debu EAF, Uji SEM, Uji Kuat Tekan, Uji TCLP ABSTRACT Slag residu and EAF dust are waste of smelting steel. This Smelting Company produce slag 6480 tons/year abd EAF dust reach the volume 1680 m 3year . Slag residu is collected then taken by third side, but EAF dust is only dumped in the ground. According to direct interview to workers, known that all workers have sick complaint which cause by this waste. Therefore, this research needed. The purpose of this research are to identifying heavy metals composition in slag residu and EAF dust with SEM test, to knows the influence of slag residu and EAF dust adding in compressive strength, and to knows the result of TCLP test of concrete. The activity of this research such as material test, mix design calculation, making of concrete, compressive strength test, anf TCLP test. The percentage of slag residu are 0%, 10%, 20%, 30% and 40% from the weight of coarse aggregate and EAF dust are 0% and 10% from the weight of cement. The result of this research in aspec of heavy metals composition taken from SEM test that exist in slag residu are Fe (47,94%); Cr (0,2%); Mn (1,618%) and EAF dust are Fe (32,443%); Zn (31,215%); Mn (4,265%). Compressive strength test result for normal concrete is 30 MPa from 30 MPa planning. For slag residu and EAF dust subtition materials are 35,677 MPa; 35,491 MPa; 35,237 MPa; 35,190 MPa. TCLP test declare that the concrete is safe to environment based on PP No. 101 Tahun 2014. Keyword: Slag residu, EAF dust, SEM test, Compressive strength test, TCLP test

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Teknik Keselamatan dan Kesehatan Kerja
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 21 Sep 2018 03:49
Last Modified: 21 Sep 2018 03:49
URI: http://repository.ppns.ac.id/id/eprint/1091

Actions (login required)

View Item View Item