STUDI PEMANFAATAN LIMBAH KARBON AKTIF SEBAGAI BAHAN PENGGANTI AGREGAT HALUSPADA CAMPURAN BETON RINGAN(STUDI KASUS DI PT. PETRONIKA)

Ardiansyah, Ryan (2017) STUDI PEMANFAATAN LIMBAH KARBON AKTIF SEBAGAI BAHAN PENGGANTI AGREGAT HALUSPADA CAMPURAN BETON RINGAN(STUDI KASUS DI PT. PETRONIKA). Diploma thesis, POLITEKNIK PERKAPALAN NEGERI SURABAYA.

Full text not available from this repository.

Abstract

ABSTRAK PT. Petronika merupakan perusahaan yang bergerak dalam bidang industri kimia yang menghasilkan DOP (Dioctyl phatalate), limbah yang dihasilkan yaitu limbah karbon aktif merupakan limbah beracun dengan kode limbah CA dan berwujud. Selama ini pemanfaatan limbah karbon aktif di PT. Petronika belum optimal dan dibiarkan begitu saja, sehingga membuat pekerja mengalami gangguan pernapasan, pusing, dan mual. Oleh karena itu dilakukan penelitian tentang pengolahan dan pemanfaaatan limbah karbon aktif di PT. Petronika sebagai bahan campuran pembuatan beton ringan. Pada penelitian ini, limbah karbon aktif digunakan sebagai pengganti agregat halus dengan variasi 0%, 5%,10%, 15%, dan 20. Pengujian yang dilakukan adalah pengujian material, perhitungan mix design, pembuatan beton, pengujian setting time, pengujian kuat tekan dan pengujian TCLP. Metode mix design yang digunakan yaitu SNI 03-2834-2000 dengan f’c 10 MPa dan nilai slump 8 ± 3 cm. Pada penelitian ini komposisi limbah terdiri Carbon, Oxygen, Titanium, Aluminium, dan Silicon. Jumlah limbah karbon aktif berpengaruh terhadap waktu yang dibutuhkan untuk mencapai final setting dengan waktu terlama mencapai 300 menit. Pada kuat tekan beton ringan, semua variasi beton ringan dengan campuran limbah karbon aktif memenuhi kuat tekan rencana yaitu berturut-turut sebesar 17,15 MPa; 13,11 MPa; 17,88 MPa; dan 14,85 MPa. Kandungan logam berat pada beton ringan pengganti agregat halus sebesar 15% di bawah baku mutu TCLP. Komposisi terbaik limbah sebagai campuran beton ringan adalah sebesar 15%. Kata kunci: Agregat halus,beton ringan, karbon aktif, kuat tekan, setting time, TCLP. ABSTRACT PT. Petronika is a company engaged in the chemical industry that produces DOP(Dioctylphatalate),the waste generated is activated carbon waste is toxic waste with waste code CA and tangible. During the utilization of waste activated carbon in PT. Petronika not optimal and unpunished, thus making the workers experienced respiratory problems, dizziness, and nausea. Therefore, research on waste processing and utilization of activated carbon in PT. Petronika as a mixture of lightweight concrete production. In this study, waste activated carbon is used in lieu of fine aggregate with a variation of 0%, 5%, 10%, 15%, and 20. This experiment is testing the material, calculations mixdesign,concrete production, testing setting time, compressive strength testing and TCLP testing.method Mix design used is SNI 03-2834-2000 with f'c 10 MPa and a slump value of 8 ± 3 cm. In this study the composition of the waste consists of Carbon, Oxygen, Titanium, Aluminum and Silicon.The amount of waste activated carbon affects the time it takes to reach the final set with the longest time of 300 minutes. In the lightweight concrete compressive strength, all variations of the lightweight concrete with a mixture of activated carbon waste meets the compressive strength of the plan is a row of 17.15 MPa; 13.11 MPa; 17.88 MPa; and 14.85 MPa. The content of heavy metals in lightweight concrete replacement fine aggregate by 15% below the quality standard of the TCLP. The best composition of waste as a lightweight concrete mix is 15%. Keywords : Fine aggregate, lightweight concrete,activated carbon, , compressive strength, setting time, TCLP.

Item Type: Thesis (Diploma)
Subjects: T Technology > T Technology (General)
Divisions: Teknik Keselamatan dan Kesehatan Kerja
Depositing User: Unnamed user with email repository@ppns.ac.id
Date Deposited: 21 Sep 2018 03:32
Last Modified: 21 Sep 2018 03:32
URI: http://repository.ppns.ac.id/id/eprint/1083

Actions (login required)

View Item View Item